Conductive Silver AG15 and Thinner

Conductive Silver AG15 is a silver-based shielding coating which provides electromagnetic compatibility (EMC) and has been specifically designed to give increased coverage while maintaining a very high conductivity. It is a very economic means of achieving excellent shielding against radiated electromagnetic interference (EMI) and maintains its low resistance even after exposure to heat, cold, humidity and salt spray. Air drying system that requires no primer or top coat. It is easily applied by spray or included brush and is compatible with plastics commonly used for electronic equipment enclosures.

For production runs, conventional forced drying methods may be used for faster processing. Forced drying will improve conductivity.

Conductive Silver AG15 dries to touch in about 10 minutes and can be handled after a further 10 minute hold, depending on surrounding temperature.

Good coating properties achieved after 4 to 8 hours air drying, depending on coating thickness and temperatures.

Key properties

• Maintains low resistance after exposure to the elements
• Comes with brush applicator, but can be sprayed
• No primer or top coat required
• Surface to be coated must be dry and free of contaminants such as oil or chemical residues.
• Recommended drying cycle: 30 Minutes @ 70 to 80°C
• Operating temperature until 105°C
• EMI shielding performance: from 10- 15µm coating thickness (recommended)
• For spray application use MEK/Diacetone Alcohol blend (2 parts w/w product to 1 part solvent); if this blend evaporates too quickly, reduce the amount of Diacetone Alcohol (DAA). recommended spray pressure of 2 to 2.5 bar, nozzle diameter varying from 1 to 1.5 mm

Specifications